Super Fine Brass powder
- Composition
- Copper: 60%, Zinc: 40%
- Manufacturing method
- Water atomization method
- Application example
- Sintered parts
Typical data
Product name | Particle size |
Tap density (Mg/m³) |
Surface area (m²/g) |
Particle size distribution(by Microtrac) | Chemical composition | ||||
---|---|---|---|---|---|---|---|---|---|
Accumulative 10% diameter (µm) |
Accumulative 50% diameter (µm) |
Accumulative 90% diameter (µm) |
Maximum diameter (µm) |
O (mass%) |
Zn (mass%) |
||||
SF-BS6040 | 10µm | 3.7 | 0.8 | 4.4 | 10.7 | 20.4 | 55.4 | 0.4 | 40.3 |
Brass powder
- Composition
- BS8020 Copper: 80%, Zinc: 20%
BS7030 Copper: 70%, Zinc: 30%
- Manufacturing method
- Water atomization method
- Application example
- Sintered oil-impregnated bearing (BS8020)
Typical data
Product name | Particle size |
Apparent density (g/cm³) |
Flow rate (s/50g) |
Particle size distribution(mass%) | Chemical composition | ||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|
+300µm | +180µm | +150µm | +106µm | +75µm | +63µm | +45µm | -45µm |
Cu (mass%) |
Zn (mass%) |
||||
BS8020 | -100# | 3.00~3.35 | <25 | - | <0.1 | <0.2 | <7 | 12~18 | 10~15 |
18~25 |
40~53 |
80 |
20 |
BS7030 | -100# | 2.90~3.30 | <25 | - | <0.1 | <0.2 | <7 | 15~22 | 10~15 |
18~25 |
30~45 |
70 |
30 |